304L cold rolled stainless steel sheet

Haosteel is professional manufacturer and supplier of 304L cold rolled stainless steel sheet. Quality guaranteed, On-time delivery, After-sales warranty. 

 

Standard: 

ASTM A240 A666

Grade:

304L

Delivery:

Cold rolled  Hot rolled

Surface:

Black/Bright/2B/BA/ NO.1/Hairline/Mirror

Thickness:

0.25-3mm

Width:

1m-3m

Length: 

2m-12m

Mill:

Tisco, Jisco, Baosteel, etc.

Delivery time:

15days in common

 

Description:

Alloy 304L a T-300 series stainless steel austenitic, which has a minimum of 18% chromium and 8% nickel. Type 304L has a carbon maximum is 0.030. It is the standard “18/8 stainless” that is commonly found in pans and cooking tools. Alloys 304L is the most versatile and widely used alloy in the stainless steel family. Ideal for a wide variety of home and commercial applications, Alloys 304L exhibits excellent corrosion resistance and has a high ease of fabrication, outstanding formability. The austenitic stainless steels are also considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes.

 

Chemical composition:

C

Si

Mn

P

S

Cr

Ni

N

≤ 0.03

≤ 1.00

≤ 2.00

≤ 0.045

≤ 0.03

18.0 - 20.0

8.0 - 10.5

≤ 0.10

 

Physical Properties:

Annealed:
Ultimate Tensile Strength – 70 KSI min (485 MPA min)
Yield Strength (0.2% Offset) –25 KSI min (170 MPA min)
Elongation – 40% min
Hardness – HRB92 max (210HV max) 

 

Tempered Condition:

The use of chip breakers is advised since the chips can be stringy. Stainless steel work harden rapidly, heavy positive feeds, sharp tooling, and a rigid set-up should be used.of cut below the work-hardened layer resulting from the previous passes.

 

Corrosion Resistance:

At times, alloy 304L may show a lower corrosion rate than the higher carbon Alloy 304; otherwise, the 304, 304L, and 304H may be considered to perform uniformly in most corrosive environments. Alloy 304L is preferred for use in environments sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones on susceptible alloys.