420 hot rolled stainless steel plate
420 hot rolled stainless steel plate
Haosteel is professional manufacturer and supplier of 430 hot rolled stainless steel plate. Quality guaranteed, On-time delivery, After-sales warranty.
|
Standard: |
ASTM A240 A666 |
|
Grade: |
420 |
|
Delivery: |
Cold rolled Hot rolled |
|
Surface: |
Black/Bright/2B/BA/ NO.1/Hairline/Mirror |
|
Thickness: |
2.5 - 100mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15days in common |
Description:
Grade 430 is a ferritic, straight chromium, non-hardenable grade, combining good corrosion resistance and formability characteristics with useful mechanical properties. Its ability to resist nitric acid attack permits its use in specific chemical applications but automotive trim and appliance components represents its largest fields of application.
Grade 430F is the free-machining version of this grade, available in bar form for use in automatic screw machines. Grade 434 is the molybdenum bearing version of Grade 430 and has the same useful combination of properties. Its molybdenum addition improves corrosion resistance.
These properties for 430 are specified for flat rolled product (plate, sheet and coil) in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as forgings and bar in their respective specifications. Properties of Grade 430F are specified for bar in ASTM A582.
Chemical composition:
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
|
0.15-0.40 |
≤ 1.00 |
≤ 1.00 |
≤ 0.04 |
≤ 0.03 |
12.0-14.0 |
≤ 0.75 |
≤ 0.50 |
Physical Properties:
Annealed:
Ultimate Tensile Strength – 10KSI min (690 MPA min)
Yield Strength (0.2% Offset) –60 KSI min (414 MPA min)
Elongation – 15% min
Hardness – HRB96max (217HV max)
Applications:
Architectural, automotive parts, cooking utensils, fasteners, food processing, oil burners parts, television cones, tobacco machinery parts.
Corrosion Resistance:
420 provides full corrosion resistance only in the hardened or hardened and tempered. In these conditions, its corrosion resistance is similar to type 410. Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Heat treatment:
Alloy 420 can be hardened by cold working and by heat treating. Please refer to Haosteel Technical Services Department for more information. Alloy 420 is capable of being heat treated to a hardness of HRC 51 minimum.